Home > Sheet and Plates > Stainless Steel 301 Sheet and Plates
Weston Stainless, Midland, UK, is a prominent supplier and producer of high-grade stainless steel products, with expertise in precision-engineered materials for industries such as construction, automotive, and aerospace. Among its products, Stainless Steel 301 Sheets and Plates are renowned for their superior corrosion resistance, high strength, and durability. Produced in Grade 301, these sheets and plates are found in a variety of shapes such as coils, strips, and cut to size, suitable for applications with great forming and welding characteristics. Composed of high-quality austenitic stainless steel, these products offer great mechanical properties for ensuring reliability and performance in extreme environments.
Stainless Steel 301 Plates and Sheets consist of Chromium (16-18%), Nickel (6-8%), Carbon (≤0.15%), Manganese (≤2%), Silicon (≤1%), and traces. Their physical properties are a tensile strength of 515-930 MPa, yield strength of 205 MPa (annealed), and elongation of 40%. They possess high hardness and superior fatigue strength. Physical properties are 7.86 g/cm³ for density, 16.3 W/m·K for thermal conductivity, and 1400-1455°C as the melting point. These properties allow them to be applicable in high-stress conditions that need resistance against corrosion and endurance.
| Item | Stainless Steel 301 sheet(Hot rolled, cold rolled) | |
| Thickness | 0.3~10.0mm | |
| Width | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc | |
| Length | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc | |
| Standard | JIS, AISI, ASTM, GB, DIN, EN, etc | |
| Surface | the surface and finish of stainless steel 301 sheet: 2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc | |
| Brand: | Indian Origin, European Origin, Japanese Origin, US Origin, Korea Origin, Thailand Origin, Taiwan Origin | |
| Package | Shrink-wrapped ,Carton boxes,Wooden pallets,Wooden boxes ,Wooden crates Etc. required. |
|
Element |
Percent by Weight |
|
|
Type 301 ANN |
||
|
Carbon |
0.150 maximum |
|
|
Manganese |
2.000 maximum |
|
|
Phosphorus |
0.045 maximum |
|
|
Sulfur |
0.030 maximum |
|
|
Silicon |
1.00 maximum |
|
|
Chromium |
16.00 – 18.00 |
|
|
Nickel |
6.000 – 8.000 |
|
|
Nitrogen |
0.10 maximum |
Contact us to get a quick quote for your requirement.
The sheets have moderate corrosion resistance, produced by high temperature rolling. They are typically available from thickness ranging from 3mm to 12mm with widths up to 2000mm and are applicable for structural applications requiring good toughness.
The superior corrosion resistance is provided by cold rolled plates, which are processed at room temperature, thus offering a smooth surface and precise thickness. The common dimensions are from 0.5mm to 6mm in thickness and widths up to 1500mm. They are suitable for high-precision applications.
These plates come with a textured surface to have grip and last longer. They come in a thickness range that is between 1.5mm and 5mm and sizes that are standard are 1000mm x 2000mm. It is suitable for flooring and anti-slip application.
Good corrosion resistance, perforated sheets feature holes punched in various patterns, enhancing aesthetics and ventilation. Sizes usually range from 0.8mm to 3mm in thickness and can be customized up to 1500mm widths and used for filtration and decorative purposes.
Thin sheets with excellent corrosion resistance, often used to fill gaps or adjust clearances in machinery. These are available from 0.1mm up to 1mm in thickness and in standard sizes of 1000mm x 2000mm. Useful for precision alignment.
Polished plates are excellent for aesthetic applications and offer high corrosion resistance with a high gloss finish. Common thicknesses range from 1mm to 10mm, and sizes typically run to 1500mm x 3000mm. They are also used in architectural and decorative projects.
Stainless Steel 301 Sheets and Plates contain Chromium (16-18%), Nickel (6-8%), Carbon (≤0.15%), Manganese (≤2%), Silicon (≤1%), and trace elements. Their mechanical properties are tensile strength of 515-930 MPa, yield strength of 205 MPa (annealed), and elongation of 40%. They are very hard in nature and possess superior fatigue strength. Physical properties are a density of 7.86 g/cm³, thermal conductivity of 16.3 W/m·K, and melting point of 1400-1455°C. These characteristics make them appropriate for high-stress applications that demand corrosion resistance and durability.
Stainless Steel 301 Sheets and Plates are supplied with test certificates, such as Mill Test Certificates (MTC), third-party inspection reports, and ASTM/ASME standard compliance for quality and authenticity. They are packaged securely in wooden crates, pallets, or waterproof wrapping to ensure they are not damaged while in transit. The delivery is efficient and fast, with domestic and international market coverage using reliable logistics for timely and safe delivery.